Heat shrink thin wall tube

HST 001 is environment friendly, flexible, flame-retardant, irradiated crosslinking heat-shrinkable modified polyolefin tubing. This high-reliability product is widely used for insulation or jacketing of wire harness, strain relief of wire terminations and connections, bundling of wire harness, protection of soldered points, insulation and capsule of electronic components, anti-corrosive protection, identification and color coding, etc

·Shrink ratio: 2:1.

·Very flexible, flame-retardant.

·Low shrink temperature.

·Good thermal stability.

·Excellent physical, chemical and electrical properties.

·Wide range of sizes and colors.

Property

Unit

Test Method

Test Value

Shrinking properties

Longitudinal Changes

%

UL 224

0 to -3 %

Eccentricity

%

UL 224

10 to 25 %

Physical properties

Tensile strength

MPa

ASTM D 2671

Min. 11MPa

Elongation

%

ASTM D 2671

Min 400 %

Heat aging

　

ASTM D 2671

　

Tensile strength

　Mpa

158℃ /168 hr

　Min. 12 Mpa

Ultimate Elongation

%

　

Min. 250%

Heat shock

　

UL 224

No cracking, flowing,

250℃ / 4 hrs

dropping

Cold bend test

　

UL 224

No cracking

-30℃ / 1 hrs

Electrical properties

Dielectric strength

kV/mm

IEC 243

32

Volume resistance

Ω.cm

IEC 93

1014

Size(mm)

As supplied(mm)

After recovery (mm)

Standard length  (m/spool)

Inside diameter

Wall thickness

Inside diameter（max.）

Wall thickness（min.）

φ0.6

0.9±0.2

0.20±0.05

≤0.40

0.33±0.10

200

φ0.8

1.1±0.2

0.20±0.05

≤0.50

0.33±0.10

200

φ1.0

1.5±0.2

0.20±0.05

≤0.65

0.36±0.10

200

φ1.5

2.0±0.2

0.20±0.05

≤0.85

0.36±0.10

200

φ2.0

2.5±0.2

0.25±0.05

≤1.00

0.45±0.10

200

φ2.5

3.0±0.2

0.25±0.05

≤1.30

0.45±0.10

200

φ3.0

3.5±0.2

0.25±0.05

≤1.50

0.45±0.10

200

φ3.5

4.0±0.2

0.25±0.05

≤1.80

0.45±0.10

200

φ4.0

4.5±0.2

0.25±0.05

≤2.00

0.45±0.10

200

φ4.5

5.0±0.2

0.30±0.08

≤2.30

0.56±0.10

100

φ5.0

5.5±0.2

0.30±0.08

≤2.50

0.56±0.10

100

φ5.5

6.0±0.2

0.30±0.08

≤2.75

0.56±0.10

100

φ6.0

6.5±0.2

0.30±0.08

≤3.00

0.56±0.10

100

φ7.0

7.5±0.3

0.30±0.08

≤3.50

0.56±0.10

100

φ8.0

8.5±0.3

0.30±0.08

≤4.00

0.56±0.10

100

φ9.0

9.5±0.3

0.30±0.08

≤4.50

0.56±0.10

100

φ10

10.5±0.3

0.30±0.08

≤5.00

0.56±0.10

100

φ11

11.5±0.3

0.30±0.08

≤5.50

0.56±0.10

100

φ12

12.5±0.3

0.30±0.08

≤6.00

0.56±0.10

100

φ13

13.5±0.3

0.35±0.10

≤6.50

0.69±0.10

100

φ14

14.5±0.3

0.35±0.10

≤7.00

0.69±0.10

100

φ15

15.5±0.4

0.35±0.10

≤7.50

0.69±0.10

100

φ16

16.5±0.4

0.35±0.10

≤8.00

0.69±0.10

100

φ17

17.5±0.4

0.35±0.10

≤8.50

0.69±0.10

100

φ18

19.0±0.5

0.35±0.10

≤9.00

0.69±0.10

100

φ20

22.0±0.5

0.40±0.12

≤10.0

0.83±0.15

100

φ22

24.0±0.5

0.40±0.12

≤11.0

0.83±0.15

100

φ25

26.0±0.5

0.45±0.15

≤12.5

0.89±0.15

50

φ28

29.0±0.5

0.45±0.15

≤14.0

0.89±0.15

50

φ30

31.5±1.0

0.50±0.15

≤15.0

1.00±0.15

50

φ35

36.5±1.0

0.50±0.15

≤17.5

1.00±0.15

50

φ40

41.5±1.0

0.55±0.15

≤20.0

1.00±0.15

50

φ45

46.5±1.0

0.55±0.15

≤22.5

1.00±0.15

25

φ50

≥50

0.55±0.15

≤25.0

1.10±0.15

25

φ60

≥60

0.60±0.15

≤30.0

1.20±0.15

25

φ70

≥70

0.65±0.15

≤35.0

1.30±0.20

25

φ80

≥80

0.65±0.15

≤40.0

1.30±0.20

25

φ90

≥90

0.65±0.15

≤45.0

1.30±0.20

25

φ100

≥100

0.65±0.20

≤50.0

1.30±0.20

25

φ120

≥120

0.65±0.20

≤60.0

1.30±0.20

25

φ150

≥150

0.65±0.20

≤70.0

1.30±0.20

25

φ180

≥180

0.65±0.30

≤90.0

1.30±0.30

25

φ210

≥210

0.65±0.30

≤105.0

1.30±0.30

25

φ230

≥230

0.65±0.30

≤115.0

1.30±0.30

25

φ250

≥250

0.65±0.30

≤125.0

1.30±0.30

25

D* = Inner diameter as supplied

d* = Inner diameter after fully recovered